Welding material
Product serial number
1
Product description
Parameters
| Welding Rod Series | |||||||||||
| Grade |
Chemical composition of deposited metal（%）
|
performance | |||||||||
| Mechanical behavior | standard value | guarantee value | |||||||||
|
FirmKim
|
FK422
|
Alloy standard |
C ≤ 0.2
|
Mn ≤ 1.2
|
Si ≤ 1.0
|
P ≤ 0.04
|
S ≤ 0.035
|
RM(MPa)
|
430-560
|
480
|
|
|
GB/T
|
E4303
|
guarantee value |
0.065
|
0.45
|
0.17
|
0.021
|
0.018
|
"ROL/Rp0.2(MPa)" |
≥ 330
|
390
|
|
|
AWS
|
/
|
Alloy standard |
Ni ≤ 0.3
|
Cr ≤ 0.2
|
Mo ≤ 0.3
|
V ≤ 0.08
|
A(％ )
|
≥ 22
|
28
|
||
| guarantee value |
0.015
|
0.008
|
0.006
|
0.01
|
KV2(J)
|
≥ 47/-20
|
82 | ||||
| Product description and main application | FK422 is a carbon steel electrode with titanium calcium coating. Both AC and DC can be used for all-position welding. It has excellent welding process performance and good mechanical properties; stable arc, small spatter, easy to remove slag, and easy to start arc again; beautiful welding seam shape, welding wave can be wide, narrow, thin, thick, easy to weld, and efficient High; used for welding important low-carbon steel structures and low-alloy steel structures with low strength grades, such as Q235, 09MnV, 09Mn2, etc. | ||||||||||
| Grade |
Chemical composition of deposited metal（%）
|
performance | |||||||||
| Mechanical behavior | standard value | guarantee value | |||||||||
|
FirmKim
|
FK502
|
Alloy standard |
C ≤ 0.15
|
Mn ≤ 1.25
|
Si ≤ 0.90
|
P ≤ 0.04
|
S ≤ 0.035
|
RM(MPa)
|
≥ 490
|
530
|
|
|
GB/T
|
E5003
|
guarantee value |
0.1
|
0.76
|
0.27
|
0.022
|
0.015
|
"ROL/Rp0.2(MPa)" |
≥ 400
|
450
|
|
|
AWS
|
/ | Alloy standard |
Ni ≤ 0.3
|
Cr ≤ 0.2
|
Mo ≤ 0.3
|
V ≤ 0.08
|
A(％ )
|
≥ 20
|
24
|
||
| guarantee value |
0.025
|
0.036
|
0.01
|
0.008
|
KV2(J)
|
≥ 47
|
96
|
||||
| Product description and main application | FK502 is a carbon steel electrode with titanium calcium coating. Both AC and DC can be used for all-position welding. It has excellent welding process performance and mechanical properties, stable arc, little spatter, and easy slag removal; welding seam Beautifully shaped; mainly used for welding low-alloy steel structures with a tensile strength of 490MPa, such as rebar for construction and other structural steels such as 16Mn. |
||||||||||
| Grade |
Chemical composition of deposited metal（%）
|
Reference current（AC、DC+）
|
Precautions | ||||||||
|
FirmKim
|
FK266
|
Alloy standard |
C ≤ 1.10
|
Mn11.00~18.002 |
Si ≤ 1.30
|
Mo ≤ 2.50
|
Total amount of other elements | Electrode diameter（mm） |
Φ3.2
|
Φ5.0
|
1. The electrode must be baked at 300~350℃ for 1h before welding. 2. For surfacing welded high-manganese steel workpieces, the fatigue layer should be removed in advance or treated with water toughening or chrome-manganese steel welding rods (such as D277) should be used for bottoming. 3. There is a lot of yellow smoke during surfacing, so attention should be paid to strengthen ventilation and operate from an upwind position. |
|
GB/T
|
EDMn-B-16
|
guarantee value |
0.65
|
14.6
|
0.75
|
1
|
≤ 1.00
|
Welding current（A） |
70~90
|
150~180
|
|
|
AWS
|
EFeMn-B
|
||||||||||
| Product description and main application | FK266 is a low-hydrogen potassium type coating high-manganese steel surfacing electrode. It can be used for both AC and DC (when AC welding, the no-load voltage is not less than 70V). It is advisable to use small current and narrow bead when surfacing. Hammer immediately Or water quenching to reduce the tendency of cracks. The surfacing metal is austenitic high manganese steel, which has the characteristics of work hardening, toughness and wear resistance. Since Mo is added to the weld metal, crack resistance and wear resistance are improved; It is suitable for surfacing welding of various crushers, high manganese steel rails, buckets, bulldozers and other parts that are subject to impact and easy to wear. |
||||||||||
| Grade |
Chemical composition of deposited metal（%）
|
Reference current（AC、DC+）
|
Precautions | ||||||||
|
FirmKim
|
FK022
|
Alloy standard |
C ≤ 0.04
|
Mn：0.5-2.5
|
Si ≤ 1
|
P ≤ 0.04
|
S ≤ 0.030
|
RM(MPa)
|
≥ 490
|
550
|
1. The electrode must be baked at 300℃ before welding 1 Hours, use as you bake. 2. When welding, try to use small current and short Arc welding. 3. Before welding, the weldment must be cleaned of rust, Impurities such as oil and moisture. |
|
GB/T
|
E316L-16
|
guarantee value |
0.024
|
0.96
|
0.55
|
0.02
|
0.004
|
||||
|
AWS
|
E316L-16
|
Alloy standard | Ni：11-14 |
Cr：17-20
|
Mo：2.0-3.0 |
Cu ≤ 0.75
|
A(％ )
|
≥ 25
|
40
|
||
| guarantee value |
13.2
|
18
|
2.2 |
0.035
|
KV2(J)
|
≥ 31
|
38
|
||||
| Product description and main application | FK022 rutile type coating of ultra-low carbon stainless steel electrode, its weld metal has good mechanical properties and resistance to intergranular corrosion, especially has good impact toughness at -196 ℃, AC and DC dual purpose, The electrode has redness resistance, soft arc, beautiful shape, good slag removal, small spatter, excellent all-position welding performance, and good operability; it is used for welding 316L austenite serving at ultra-low temperature of -196℃. Rusty steel piping system. Suitable for welding of liquefied natural gas (LNG) storage tanks and pipelines, and cryogenic pressure equipment. |
||||||||||
| Gas shielded solid wire | |||||||||||
| Grade |
Chemical composition of deposited metal（%）
|
performance | |||||||||
| Mechanical behavior | standard value | guarantee value | |||||||||
|
FirmKim
|
FK70S-6
|
Alloy standard |
C：0.06-0.15
|
Mn:1.4-1.85 |
Si:0.8-1.15
|
P ≤ 0.025
|
S ≤ 0.025
|
RM(MPa)
|
≥ 500
|
545
|
|
|
GB/T
|
ER50-6
|
guarantee value |
0.077
|
1.54
|
0.92
|
0.011
|
0.011
|
"ROL/Rp0.2(MPa)" |
≥ 420
|
445
|
|
|
AWS
|
ER70S-6
|
Alloy standard |
Ni ≤ 0.15
|
Cr ≤ 0.15
|
Mo ≤ 0.15
|
V ≤ 0.03
|
Cu ≤ 0.5
|
A(％ )
|
≥ 22
|
31
|
|
| guarantee value |
0.006
|
0.023
|
0.004
|
0.002
|
0.126
|
KV2(J)
|
≥ 27
|
≥ 27
|
|||
| Product description and main application | Strong resistance to scale and oil on the surface of the base material, and low pore sensitivity; suitable for welding of structural steels of corresponding strength levels | ||||||||||
| Gas shielded flux cored wire | |||||||||||
| Grade |
Chemical composition of deposited metal（%）
|
performance | |||||||||
| Mechanical behavior | standard value | guarantee value | |||||||||
|
FirmKim
|
FK501-1
|
Alloy standard |
C ≤ 0.18
|
Mn ≤ 2.00
|
Si ≤ 0.90
|
P ≤ 0.030
|
S ≤ 0.030
|
RM(MPa)
|
490 ～ 670
|
560
|
|
|
GB/T
|
T494T1-1C
|
guarantee value |
0.05
|
1.28
|
0.35
|
0.011
|
0.009
|
"ROL/Rp0.2(MPa)" |
≥ 390
|
490
|
|
|
AWS
|
E71T1-C1
|
Alloy standard |
Ni ≤ 0.50
|
|
A(％ )
|
≥ 18
|
28
|
||||
| Example value |
0.42
|
KV2(J)
|
≥ 27
|
130
|
|||||||
| Product description and main application | Titanium oxide CO2 gas shielded flux-cored welding wire has excellent welding performance, soft and stable arc, small spatter, easy slag removal, and beautiful weld shape. Suitable for flat welding and horizontal welding, can be carried out All-position welding, high welding efficiency. The deposited metal has been toughened with trace elements and has excellent low temperature toughness and good crack resistance; suitable for shipbuilding, machinery manufacturing, petroleum machinery, chemical machinery, Welding of important positions of carbon steel and low-alloy structural steel such as hoisting machinery. |
||||||||||
| Submerged arc welding wire | |||||||||||
| Grade |
Chemical composition of deposited metal（%）
|
performance | |||||||||
| Mechanical behavior | standard value | guarantee value | |||||||||
|
FirmKim
|
FK10Mn2
|
Alloy standard |
C ≤ 0.12
|
Mn:1.5-1.9
|
Si ≤ 0.70
|
P ≤ 0.03
|
S ≤ 0.03
|
RM(MPa)
|
490~670
|
符合标准
|
|
|
GB/T
|
F5A2-H10Mn2
|
Example value |
0.066
|
1.62
|
0.011
|
0.011
|
0.011
|
"ROL/Rp0.2(MPa)" |
≥ 390
|
490
|
|
|
AWS
|
F7A0-EH14
|
Alloy standard |
Ni ≤ 0.3
|
Cr ≤ 0.2
|
Cu
|
A(％ )
|
≥ 18
|
28
|
|||
| guarantee value |
0.007
|
0.013
|
0.12
|
KV2(J)
|
≥ 27
|
130
|
|||||
| Product description and main application | High-manganese welding wire, matched with low-manganese and silicon fluxes, is not sensitive to rust on the base metal, and has excellent weld bead formation and slag removal performance. Single, bipolar, AC and DC welding are possible; it is matched with high manganese welding wire, and low manganese, silicon flux, insensitive to rust on the base metal, and has excellent weld bead formation and slag removal performance. Single, bipolar, AC and DC welding are acceptable; with sintered flux 101, both high-speed welding and filling welding of base materials with 500MPa tensile strength can be used. It has very stable mechanical properties of deposited metal. | ||||||||||
| Flux | |||||||||||
| Grade |
Chemical composition of deposited metal（%）
|
performance | Precautions | ||||||||
| Mechanical behavior | standard value | guarantee value | |||||||||
|
FirmKim
|
FK303GS
|
Alloy standard |
SiO2+TiO2
|
Al2O3+MnO
|
CaF2
|
S
|
P
|
RM(MPa)
|
430 ～ 600
|
450
|
1. The flux is in Before use 300 ～ 350℃ baking Bake for 2h. 2. The welding should be removed before welding Rust and oil on parts Impurities such as dirt and moisture. |
|
GB/T
|
AR-SU08A
|
Example value |
30
|
59
|
8.8
|
0.022
|
0.021
|
"ROL/Rp0.2(MPa)" |
≥ 330
|
355
|
|
|
AWS
|
F6A0-EL8
|
guarantee value | - | - | - |
≤ 0.050
|
≤ 0.060
|
A(％ )
|
≥ 20
|
29
|
|
|
KV2(J)
|
≥ 27
|
100
|
|||||||||
| Product description and main application | KF303GS is an aluminum-silicon type acid sintered flux with a basicity of about 1.0, and the flux is round particles with a particle size of 2.0 ~ 0.28mm (10 ~ 60 mesh). Has excellent welding process performance, The arc combustion is stable, the slag removal is good, and the weld seam is beautifully formed. The flux has strong anti-porous ability and is not sensitive to a small amount of rust and high temperature oxide film. It can be used for both AC and DC, welding when DC welding Wire the positive electrode. The welding speed can reach 2 meters per minute; with appropriate welding wire (such as H08A, H08MnA, H08MnMoA), it can weld low-carbon steel and low-alloy steel structures, such as ships, Boilers, pressure vessels; especially suitable for high-speed welding of thin plates. |
||||||||||
Previous
Flux core solder
Next
Tin solder
Tel: 0571-88780081
Mail: Firmkim@cn-huaguang.com
Fax: 0571-887 80081
Post code: 311112
Add: No. 7 Yaojia Road, Liangzhu Street, Yuhang District, Hangzhou City, Zhejiang Province (Huaguang New Materials)
Douyin QR code
We chat number
WeChat public account
PC_link：
©2021 Hangzhou Fujing Welding Technology Co., Ltd. all rights reserved 浙ICP备2021023610号-1 300.cn Hangzhou
-
WeChat
-
Telephone
- Service Hotline 0571-88780081
- TOP